If you are looking for дистрибьюторы алюминиевой фольги в Китае, мы предлагаем вам выбрать Haomei Aluminium в качестве поставщика. Haomei принимает стек прокатки в производстве алюминиевой фольги, Для ультратонкой алюминиевой фольги толщиной менее 0,012 мм (толщина связана с диаметром рабочего валка), благодаря упругому уплощению валков, it is very difficult to use a single-sheet rolling method, so the double rolling method is used, то есть, the The method of adding lubricating oil between two aluminum foils and then rolling them together (also called stack rolling). Stack rolling can not only produce ultra-thin aluminum foil that cannot be produced by single rolling, but also reduce the number of breaks and improve labor productivity. Using this process, single-sided smooth aluminum foil of 0.006mm to 0.03mm can be mass-produced.

In the process of aluminum foil rolling, the phenomenon that the thickness of the foil thins with the rise of the rolling system is called the speed effect. The explanation of the speed effect mechanism still needs in-depth study. The reasons for the speed effect are generally considered to have the following three aspects:

1), The friction state between the work roll and the rolling material changes. As the rolling speed increases, the amount of lubricating oil introduced increases, so that the lubrication state between the roll and the rolling material changes. The friction coefficient decreases, the oil film becomes thicker, and the thickness of the алюминиевая фольга decreases accordingly.

2), Changes in the rolling mill itself. In a rolling mill with cylindrical bearings, as the rolling speed increases, the roll neck will float in the bearing, so that the two rolls that interact with each other under load will move in a direction close to each other.

3), The processing softens when the material is deformed by rolling. The rolling speed of the high-speed aluminum foil rolling mill is very high. As the rolling speed increases, the temperature of the rolling deformation zone is increased. According to calculations, the metal temperature in the deformation zone can rise to 200°C, which is equivalent to an intermediate recovery annealing. The processing softening of rolled materials.